2324 T39 Aluminum High Strength Plate Sheet

• Color: Silver
• Application: Transportation Tools, Door & Window, Decorations
• Certification: ISO9001, ASTM, JIS, GB, EN
• Technique: Extruded
• Grade: 2000 Series
• Temper: O - H112
• Model NO.: 2324
• Surface Treatment: Enameled Wire
• Alloy: Alloy
• Elongation: More Than 10%
• Transport Package: Export Standard Wooden Pallet
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7606125900
• Production Capacity: 20000mt/Month

Product Description

2324 t39 aluminum high strength plate sheet

 

 

Chemical Composition of 2324

Alloy

Si

Fe

Cu

Mn

Mg

Cr

Ni

Zn

Ti

Zr

Others

Al

Each

Total

2324

0.60

0.12

4.0~4.5

0.45~0.7

1.2~1.6

0.10

~

0.25

0.15

~

0.05

0.15

Remainder

Alloy	Alloy series	Main features	Σb Value/MPa	Working Temperature /ºC
2324	Al-Cu-Mg	The special T39 state thick plate has higher strength, better fracture toughness and good crack resistance than 2024-T351 plate.	390~485	<150

 

Technical indexes of 2324 aluminum alloy
Alloy	Type	Temper	δ  or d/mm	σb/MPa	σp 0.2/MPa	δ/%	KIC or KC/MPa	Technical Standard
2324	Aluminum plate	T39	19~32	475	370	8	T: 26.4 L:22.0 S-T: 19.8	-

2024Welding Property
Alloy	Resistance welding	Melting welding	Argon arc welding	Note
2324	Good	Worse	Worse	For gas welding and argon arc welding of aluminum alloy as solder, tend to form crystalline cracks; 4A01 alloy solder, forming cracks tend to be significantly reduced, but the strength of welded joint is greatly reduced, such as heat treatment after welding, the joint strength is close to the substrate, but the ductility decreases.

 

Alloy	Temper	Aircraft Types	Application parts and typical parts
2324	Aluminum plate: T39	B737-400, ARJ21, F-35	The lower wall of a wing