| Chemical composition of 2214 alloy | |||||||||||||
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Zr | Others | Al | |
| Each | Total | ||||||||||||
| 2214 | 0.50-1.2 | 0.30 | 3.9~5.0 | 0.4~1.2 | 0.2~0.8 | 0.10 | ~ | 0.25 | 0.15 | ~ | 0.05 | 0.15 | Remainder |
| Alloy | Alloy Series | Main features | Σb Value /MPa | Working temperatures /ºC |
| 2214 | Al-Cu-Mg-Si | The heat treatment can strengthen the aluminum alloy, the main varieties are rod and forgings. The iron impurity content in the alloy composition is lower than that of the 2014 alloy, and the toughness is improved. The strength of solid solution treatment plus artificial aging is higher, and the co - worker has medium plasticity. It is suitable for manufacturing high load parts with thick section. The alloy has high copper content and poor corrosion resistance. Other properties are equivalent to 2014 alloy. | 420~460 |
<150 |
| Technical indexes of 2214 aluminum alloy | ||||||||
| Alloy | Type | Temper | δ or d/mm | σb/MPa | σp 0.2/MPa | δ/% | KIC or KC/MPa | Technical standard |
| 2214 | Extruded aluminum profile | T6 | ≤140 | 460 | 400 | 7 | - | Z9-0405-1992 |
| >140~160 | 460 | 290 | 6 | - | ||||
| >160~220 | 450 | 280 | 6 | - | ||||
| 2214Welding Property | ||||
| Alloy | Resistance welding | Melting welding | Argon arc welding | Note |
| 2214 | Good | Ok | - | In the process of welding, the tendency of heat cracking is larger. Therefore, the content of iron impurities in the matrix is limited and the qualified filler can be obtained by using special filler. |
| Alloy | Temper | Aircraft type | Application parts and typical parts |
| 2214 | Aluminum round bar: T6 Aluminum forgings:T6 |
ARJ21,Z9 | Frame, frame frame |