2b50 Aluminum Forgings Forged Product Parts

• Customization: Available
• Processing Object: Metal
• Molding Style: Hot Forging
• Model NO.: 2B50
• Molding Technics: Gravity Casting
• Application: Aviation
• Material: Aluminium
• Heat Treatment: Quenching
• Surface Treatment: Zinc/Chrome Plating,Anodizing
• Forging Tolerance: +/-0.2mm
• Standard: ANSI
• Certification: CE, ISO 9001:2008
• Service: OEM ODM
• Transport Package: Export Standard Wooden Pallet or as Your Requsts
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7218100000
• Production Capacity: 5000pieces/Month

Product Description

2B50 is a high strength forged Al-Cu-Mg-Si alloy, which can be strengthened by heat treatment. The chemical composition of the alloy is slightly different from that of chromium and titanium, and the content of other elements is the same as that of 2A59 aluminium alloy. The properties of the alloy are basically the same as that of 2A50, which can be used for each other. However, the plasticity of the alloy in hot state is better than that of 2A50.


2B50 is used to make complex and moderate strength free forgings and die forgings, such as compressor impeller, fan impeller, etc.
 

Mechanical Properties of 2B50 Die Forgings and Free Forgings as stipulated in Technical Standards
	Temper	Direction	Tension strength Rm/MPa	Prescribed plastic elongation strength Rp0.2/MPa	Elongation A (%)
Free forging	T6	Portrait	365	-	9.0
	T6	Long transverse	345	-	6.0
Die forging	T6	Portrait	380	275	11.0
	T6	Long transverse	365	245	7.0

 

Tensile Properties of 2B50 Aluminum Alloy Wheel Hubs at Room Temperature
Temper	Stabilization treatment		Tension strength Rm/MPa	Elongation A (%)
	Temperature/ºC	Holding time /h
T6	Portrait	380-470	280--390	17.1
	Long transverse	380-465	275--380	15.3
	Short transverse	385-450	280--370	13.7

Torsional and shear properties of T6 forgings of 2B50 aluminium alloy
	Temper	Tension strength Rm/MPa	Prescribed plastic elongation strength  Rp0.2/MPa	Elongation A (%)
2B50 forgings	T6	335	195	255

2B50 aluminium alloy is easy to overburn, and the temperature of overburn is 545 ºC. During solution quenching, the process temperature must be strictly controlled. In addition, the transfer time should not exceed 15 s to avoid affecting the mechanical properties and corrosion resistance of the alloy. The process plasticity of the alloy in hot state is better than that of 2A50 aluminum alloy. The forging temperature range is 420-470 ºC.
 

Type	Alloy	Projected area(m2)Or weight(kg)	Temper	Standard
Free forgings	5 series	≤3000kg	O,F	GBn223     ASTMB247
	2,6,7 series	≤3000kg	T6,T4,O,F
Mould forgings	5 series	≤2.5m2	O,F
	2,6,7 series	≤2.5m2	T6,T4,O,F