8A06 Aluminum Alloy Extruded Seamless Tubes

• Customization: Available
• Type: Decoration Aluminium Profile, Transport Aluminium Profile, Industrial Aluminium Profile
• Shape: Square/Round/Flat/or as Customers′ Drawing
• Model NO.: 8A06
• Grade: 7000 Series
• Temper: T62/T6/T4/O
• Alloy: Alloy
• Surface Finishing: Mill Finish/Polished/Anodizing/Brushing
• Alloying Ingredient: 7A04/7A09/7A15/7b05
• Certification: CE, ISO, ISO9001:2008/SGS
• Polished Aluminum Profile: Mechanical Polishing
• Normal Anodizing Thickness: 8-15 Micro
• Color: Any
• Deep Process: CNC, Drilling, Milling, Cutting, Welding
• Service: OEM and ODM
• Transport Package: Ep Paper Inside, Craft Paper/Pallet Outside.
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7604210000
• Production Capacity: 10000mt/Month

Product Description

8A06 Aluminum Alloy Extruded Seamless Tubes

7A04 7A09 7A15 7B05 aluminum tube pipe is a heat treatment and strengthening alloy of Al-Zn-Mg-Cu system. Its strength is higher than that of hard aluminum. It is characterized by its yield strength close to tensile strength and plasticity, and its sensitivity to stress concentration is strong, especially when subjected to vibration load and repeated static load. Therefore, the design of parts, the manufacturing process and the assembly process need to strictly avoid the stress concentration and the formation of additional stress. The heat resistance of the alloy is poor, and it will soften rapidly when the temperature is higher than 125, and the stress corrosion resistance of thick and thick parts is poor in short and transverse.

Ultra high strength Aluminum Alloy 7A09 alloy is Al-Zn-Mg-Cu, the strength of 7A09-T6 alloy 7A09 aluminum tube pipe is the highest, the aviation industry with one of the highest strength Aluminum Alloy deformation, the composition ratio of 7A04 alloy more superior performance, so it has better, get more extensive application in aircraft manufacturing, used in the manufacture of various important components of the force,7A09 aluminum alloy sheet round bar forgings have been widely used in aircraft, transport aircraft, and medium bomber trainer, for the production of the front landing gear, wing, fuselage connection frame, beam, pillar, partitions, floors, main beam joints and tail on the wall, the working cylinder hydraulic system, hydraulic oil tank of the movable rod inside and outside the tube, and other key components. Because of its high strength, the weight reduction effect is good and the safety of the aircraft is improved.

7B05 aluminum tube pipe is a relatively mature high purity aluminum alloy in China. It is a large aluminum alloy used on  aircraft in China. Parts of the machine account for 60% of the total aluminum alloy consumption, and the consumption of the single machine is about 20t, which achieves stable batch supply. Varieties include plates, thick plates, profiles, extruded panels, bars and forgings. The successful application of 7B04 alloy to aircraft provides valuable experience for the promotion of domestic new materials in civil aircraft.

Specification:
Alloy: 7A04 7A09 7A15 7B05
Temper: T62,T6,T4,O
OD: 3--130mm
ID: 3--100mm
Length: 1000mm--6000mm
 

Chemical Composition of 7A04 7A09 7A15 7B05 aluminum tube pipe
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ga	V	Ti	Other	Min.Al
7A04	0.5	0.5	1.4-2.0	0.20-0.6	1.8-2.8	0.10-0.25	-	5.0-7.0	-	-	0.10	0.15	Remainder
7A09	0.5	0.5	1.2-2.0	0.15	2.0-3.0	0.16-0.30	-	5.1-6.1	-	-	0.10	0.15	Remainder
7A15	0.5	0.5	0.5-1.0	0.1-0.1	2.4-3.0	0.1-0.3	-	4.4-5.4	-	-	0.05-0.15	0.15	Remainder
7B05	0.3	0.35	0.20	0.20-0.7	1.0-2.0	0.30	-	4.0-5.0	-	-	0.20	0.15	Remainder

  

Physical Property of 7A04 7A09 7A15 7B05 aluminum tube pipe
Alloy	Temper	Wall thickness /mm	Room temperature Test Result
			Tension Strength/MPa	Yield Strength/MPa	Elongation/%
					A50mm	A
			Not less than
7A04 TA09	T62	≤80	530	400	-	5
	T6	≤80	530	400	-	5
7A15	T62	≤80	470	420	-	6
	T6	≤80	470	420	-	6
7B05	O	≤12.00	245	145	12	-
	T4	≤12.00	305	195	11	-
	T6	≤6.00	325	235	10	-
		>6.0-12.0	335	225	10	-