2b16 Aluminum Alloy Sheet Profile Forging

• Customization: Available
• Color: Silver
• Application: Transportation Tools, Door & Window, Decorations
• Model NO.: 2B16
• Certification: ISO9001, ASTM, JIS, GB, EN
• Technique: Extruded
• Grade: 2000 Series
• Temper: O - H112
• Surface Treatment: Enameled Wire
• Alloy: Alloy
• Elongation: More Than 10%
• Transport Package: Export Standard Wooden Pallet
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7606125900
• Production Capacity: 20000mt/Month

Product Description

 

 

 

2B16 Aluminum Alloy sheet profile forging

  

Chemical Property of 2B16 Alloy

Alloy

Si

Fe

Cu

Mn

Mg

Cr

Ni

Zn

Ti

Zr

Others

Al

Unit

Total

2B16

0.25

0.30

5.8~6.8

0.2~0.4

0.05

-

-

-

0.08~0.2

0.10~0.25

0.05

0.15

Remainder

Alloy	Alloy Series	Main features
2B16	Al-Cu-Mn	The heat treatment strengthened alloy, Al-Cu-Mn rivet alloy, is used for riveting the aeronautical spacecraft. It has good riveting performance, and it can work for a long time below 250 degrees. Its room temperature and high temperature shear strength is higher than that of 2A10 alloy. It can be used for a long time after heat treatment. The supplied wire is 1.6~10mm in diameter and is delivered in a cold hardened state. The rivets are used to riveting heat resistant structures of large missiles, large launch vehicles and aircraft after solid solution treatment and artificial aging.

 

Shear strength of 2B16-T6 alloy wire after heating for 30min at 200 ºC
Standard	Test Condition	d/mm	Tm/(Mpa) Not less than
GJB 2055	Solid solution heat treatment at 535 ºC + artificial aging 175ºC, 12h	All	275
Q/6S 113	Solid solution heat treatment at 525ºC + artificial aging 165ºC, 12h	4	275
		6	265

Calibrated shear strength of alloy wire of 2B16-T6
Standard	Test Condition	Grade	Tm/(Mpa) Not less than
GJB 2055	Solid solution heat treatment at 535 ºC + artificial aging 175 ºC, 12h	A	186
		B	177

 

Typical room temperature shear strength of alloy 2B16-T6
Type	Test Condition	d/mm	σb/MPa	σp 0.2/MPa	δ/%
Aluminum round bar	Solid solution heat treatment at 525 ºC+ artificial aging 165ºC, 12h	All	403	252	23.3
Aluminum wire	Solid solution heat treatment at 525 ºC+ artificial aging 200ºC, 12h	4	329	-	-
	Solid solution heat treatment at 525 ºC+ artificial aging 250ºC, 12h	4	275	-	-

Typical room temperature shear strength of alloy of 2B16
Test Condition	d/mm	Stabilization treatment		Shear strength Tm/(Mpa)
		Temperature/ºC	Time/h
Solid solution heat treatment at 525 ºC  + artificial aging 165 ºC  /12h	4	-	-	290
Solid solution heat treatment 535ºC + cold drawn 1%~3% deformation rate + artificial aging 175 centigrade /18h		-	-	274
Solid solution heat treatment at 535 ºC  + artificial aging 190ºC  /18h		-	-	263
Solid solution heat treatment at 525 ºC  + artificial aging 165ºC  /12h		125	100	288
		150	100	277
		175	100	240
		225	100	200
		250	100	179
		300	100	163
Solid solution heat treatment 535 ºC  + cold drawn 1%~3% deformation rate + artificial aging 175  ºC  /18h		200	100	225
Solid solution heat treatment at 535 ºC + artificial aging 190 ºC/18h		190	100	228
		200	100	222
		220	100	218
		250	100	200

 

High temperature shear strength of 2B16 alloy
Test Condition	d/mm	Stabilization treatment			Temperature/ºC	Time/h	Shear strength Tm/(Mpa)
		Temperature/ºC	Time/h
Solid solution heat treatment at 525 ºC  + artificial aging 165 ºC  /12h	4	- - -		- - -	100	30	269
					125		247
					150		232
					175		215
					200		198
					220		150
Solid solution heat treatment 535ºC + cold drawn 1%~3% deformation rate + artificial aging 175 centigrade /18h					185		194
					190		189
					200		184
					210		172
					220		156
Solid solution heat treatment at 535 ºC  + artificial aging 190ºC  /18h					185		196
					190		187
					200		178
					210		169
					220		155
					250		115
Solid solution heat treatment at 525 ºC  + artificial aging 165ºC  /12h		125		100	125	30	260
		150			150		236
		175			175		196
		225			225		121
		250			250		90
		300			300		68
Solid solution heat treatment 535 ºC  + cold drawn 1%~3% deformation rate + artificial aging 175  ºC  /18h		220			220		139
Solid solution heat treatment at 535 ºC + artificial aging 190 ºC/18h		190			190		158
		200			200		148
		220			220		137
		250			250		109