4A11/4032/5A02/5A05/5A06/5083 Forged Aluminum Wheels Auto Parts

• Customization: Available
• Processing Object: Metal
• Molding Style: Hot Forging
• Model NO.: 4A11/4032/5A02/5A05/5A06/5083
• Molding Technics: Gravity Casting
• Application: Aviation
• Material: Aluminium
• Heat Treatment: Quenching
• Surface Treatment: Zinc/Chrome Plating, Anodizing
• Forging Tolerance: +/-0.2mm
• Standard: ANSI
• Certification: CE, ISO 9001:2008
• Service: OEM ODM
• Transport Package: Export Standard Wooden Pallet or as Your Requsts
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7218100000
• Production Capacity: 5000pieces/Month

Product Description

4A11 and 4032 are Al-Si-Cu-Mg series Forged aluminium alloys. They are both forged and cast aluminium alloys. They can be strengthened by heat treatment. It has the advantages of small coefficient of thermal expansion and good wear resistance. It has good heat resistance, fatigue resistance and low temperature mechanical properties. It has good plasticity in hot state and good corrosion resistance.

4A11 and 4032 aluminium alloy forgings are mainly used to manufacture materials for piston and cylinder of steam engine, as well as complex forgings working below 200 C and bearing heavy loads.

Tensile Properties of 4A11 4032 Aluminum Alloy at Room Temperature and Low Temperature
Temper	Temperature/ºC	Tension strength Rm/MPa	Prescribed plastic elongation strength Rp0.2/MPa	Elongation A (%)
T62	-200	460	337	11
	-100	415	325	10
T62	-30	385	315	9
	25	360	290	2.5

For complex or heavy forgings, the water temperature during quenching can be increased to 65-80 ºC to avoid the deformation of forgings, but the mechanical properties will decrease.
Generally, the transfer speed during quenching should not exceed 10 s. For heavy forgings, the transfer speed should not exceed 15 s, so as to avoid affecting the mechanical properties and corrosion resistance of the alloy.
The two alloys have good plasticity in hot state. They are suitable for extrusion into bar and various interface profiles, and for making various forgings.

Type	Alloy	Projected area(m2)Or weight(kg)	Temper	Standard
Free forgings	5 series	≤3000kg	O,F	GBn223     ASTMB247
	2,6,7 series	≤3000kg	T6,T4,O,F
Mould forgings	5 series	≤2.5m2	O,F
	2,6,7 series	≤2.5m2	T6,T4,O,F

5A02 alloy has low strength and high plasticity. Cold deformation can improve its strength, but it will reduce its plasticity. It has good properties of hydrogen atom welding, contact welding and friction stir welding. It can also be gas welding and has high corrosion resistance. In aircraft manufacturing, welding under moderate loads requires high process plasticity and corrosion resistance components, such as pipes, liquid containers and sliding frames, and also used to manufacture airplane mailboxes and conduits, welding wires, rivets and ship structures.

The melting temperature and casting temperature of 5A02 are 700-750 ºCand 690-730 ºC respectively. Alloy wires are used as solders and rivets. The machinability of 5A02O is not good, and it is improved under the condition of cold work hardening. The surface treatment process of 5A02 is similar to that of other aluminium alloys, but much worse than that of 6063 alloy.


The magnesium content of 5A05 alloy is high, although cold deformation can improve its strength, but the plasticity will decrease accordingly; the O state material has higher plasticity, and the H * 4 material has medium plasticity. Although the technological plasticity of 5A05 alloy is high, the cold work hardening speed is fast in the process of cold deformation, which should be paid attention to when processing parts.

In aircraft manufacturing, the alloy is usually used to manufacture parts with high process plasticity and corrosion resistance, as well as welded pipes, liquid containers, welded structural parts, aircraft skin skeleton and so on.

5A06 alloy has the highest Mg content (6.3%) and the highest Mn content (0.65%). The average total content of Mg and Mn reaches 7%. Because of its high strength, relatively low plasticity, good corrosion resistance and weldability, it can be processed into plates, tubes, rods, profiles, wires and forgings, die forgings, etc. It has been widely used in aviation, aerospace, missiles, ships, automobiles, tanks and other industries. Mainly used for welding structure, cold forging parts, stress parts of welding vessels, aircraft skin skeleton parts and rivets.
 

5A02 5A05 5A06 Chemical Composition
Alloy	Si	Fe	Cu	Mn	Mg	Zn		Ti	Others		Al
									Each	Total
5A02	0.4	0.4	0.1	0.15~0.40	2.0~2.8	-	0.6(Si+Fe)	0.15	0.05	0.15	Rest
5A05	0.5	0.5	0.1	0.30~0.6	4.8~5.5	-	-	-	0.05	0.15	Rest
5A06	0.4	0.4	0.4	0.50~0.8	5.8~6.8	0.2	0.0001~0.005	0.02~0.10	0.05	0.15	Rest

 

Calibrated Mechanical Strength of 5A02 Alloy Semi-finished Products
Standard	Type	Temper	δ or d/mm	Tension strength Rm		A/%
				Not less than
			OD ≥50,Wall thickness≤5.0	≥215
GJB 2351	Free forging,Die forging	H112	As agreement	≥177		≥15
HB 5204
GB/T 3196 GJB 2055	Wire	H×8	1.6~10.0	≥118		-
Calibrated Mechanical Strength of 5A05 Alloy Semi-finished Products
Standard	Type	Temper	δor d/mm	Tension strength Rm/Mpa	Rp0.2/Mpa		A/%
GJB 2351	Free forging,Die forging	H112	As agreement	≥196 ≥220	- -		≥10 ≥12
Calibrated Mechanical Strength of 5A06 Alloy Semi-finished Products
Standard	Type	Temper	δor d/mm	Tension strength Rm/Mpa	Rp0.2/Mpa		A/%
GJB 2351	Free forging,Die forging	H112	As agreement	≥196 ≥220	- -		≥10 ≥12

 

Type	Alloy	Projected area(m2)Or weight(kg)	Temper	Standard
Free forgings	5 series	≤3000kg	O,F	GBn223     ASTMB247
	2,6,7 series	≤3000kg	T6,T4,O,F
Mould forgings	5 series	≤2.5m2	O,F
	2,6,7 series	≤2.5m2	T6,T4,O,F