1350 Aluminium Flat Bus Bar

• Customization: Available
• Shape: Rectangular
• Application: Electric
• Model NO.: 1350
• Certification: ISO9001, ASTM, JIS, GB, EN
• Grade: 1000 Series
• Surface Treatment: Zinc, Nickel, Tin, Silver, etc.
• Alloy: Non-alloy
• Thickness: 8-30mm
• Width: 40-400mm
• Interface Type: DC/DC
• Processing: Stamping, Bending, Drilling, Threading, Polishing
• Transport Package: Export Standard Wooden Pallet, Box
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7606119000
• Production Capacity: 15000mt/Month

Product Description

1350 aluminium flat bar

Alloys and Tempers
Pure aluminum has a conductivity of about 65 percent of the International Annealed Copper Standard (lACS). Aluminum can be produced 99.99 percent pure; however, this purity is costly to achieve and the mechanical properties are low. 
Aluminum 1350 is a commercial high-purity aluminum with 61 percent conductivity. The tensile strength of each 1350 temper is determined by the amount of work given the metal during fabrication. Today, most 1350 aluminum bus conductors are of -Hlli temper for extrusions, -H112 for sawed rolled plate, and -F for cast bars.
The designations 1350-F and 1050 are often used in the trade for designating cast bus bars made by run-out into sand molds,or continuous run-out through an orifice.
  

Alloy	1350		Temper	O
Thickness (mm)	0.2-0.3	0.4-0.8	1.0-2.0	2.0-3.0
Width (mm)	<100	100-200	201-500	500-1300
Mechanical Property
U.T.S.	Density in 20ºC		Max. Resistance in 20ºC
60-95N/mm2	2.703kg/dm3		≤0.02825Ωmm2/m

Flatwise Bending Radius
 

Type of Bar	Alloy and Temper	Thickness  in.	Radius  min.
	1350-H11	All	1 * thickness
Extruded	6101-H11	0.250-0.750 0.751-1.000	1 * thickness 2 * thickness
	6101-T6	0.125-0.375 0.376-0.500	2 * thickness 21/2 thickness
	6101-T61	0.125-0.500 0.501-0.749 0.750-1.000 1.001-1.625	1 * thickness 2 * thickness 3 * thickness 4 * thickness
	6101-T63	0.125-0.375 0.376-0.500 0.501-1.000	1 * thickness 11/2 thickness 21/2 thickness
	6101-T64	0.125-0.750 0.751-1.000	1 * thickness 2 * thickness
	6101-T65	0.125-0.500 0.501-0.749	1 * thickness 2 * thickness
Rolled	1350-H12	All	1 * thickness
Sawed plate	1350-H112	All	1 * thickness

 
 Applicable to widths up through 6 inches in the T6,T61,T63 and T65 temper and to widths up through 12 inches for all other listed tempers. Bend radius for greater widths are subject to inquiry.

Chemical  Composition

Si	Fe	Cu	Mn	Mg	Cr	Zn	V+Ti	Others		Al.
								Individual	Total
Max. 0.10	Max. 0.40	Max. 0.05	Max. 0.01	-	Max 0.01	Max. 0.05	Max. 0.02	Max. 0.03	Max 0.10	Min. 99.50

Properties
Aluminium and Copper Specifications

Definitions :
Specific Heat: The heat required to raise the temperature of its unit by mass by 1ºC.(This is a physical property)
Density: This is it's mass per unit volume. This is defined as mass divided by volume.
Melting Point: The point at which it changes state from a solid to a liquid.
Ultimate Tensile Strength: The maximum stress value as obtained on a stress-strain curve.
Ultimate Shearing Strength: The force that will shear the material, and act in the plane of the area at a right angle to the area subjected at such force.
Elastic Modulus: The ratio of the unit stress to the unit strain within the proportional limits of a material in tension or compression.
0.2% Tensile-proof Strength: (yield strength) The point between 60- 80% of the ultimate tensile strength of the material where a 0.2% permanent deformation will occur.
Coefficient of Expansion: This is the fractional change in length per degree of temperature change.
IACS: International Annealed Copper Standard.

Specifications :
low price aluminum bar
thickness:0.2~12.0mm
width:500~1200mm
sample: free and fast
ISO9001-2008,SGS
offer tailor-made spec.

Rectangular angle aluminium busbar
3mm (thickness)	3*15	3*20	3*25	3*30	3*40	3*50
4mm (thickness)	4*10	4*20	4*25	4*30	4*40	4*45	4*50
5mm (thickness)	5*20	5*25	5*30	5*35	5*40	5*50	5*60	5*80
6mm (thickness)	6*20	6*30	6*40	6*50	6*60	6*80	6*100	6.3*50	6.3*80	★6.3*100
7mm (thickness)	7.6*80								6.3*76	★6.3*63
8mm (thickness)	8*11	8*30	8*40	8*50	8*60	★ 8*63	8*80	8*100	8*120	8.1*74
10mm (thickness)	10*30	10*40	10*50	10*60	★10*63	10*80	10*100	10*120	10*125	10*140
	10*150	10*160
12mm (thickness)	★12*60	★12*80	★12*100	12*120	★ 12*125	12*150	★ 12.5*125
14mm (thickness)	★14*80	★14*100		Square rod	★ 50*50	★ 35*55	19*19	Six angle rod	★30	★40
15mm (thickness)	15*100	15*120		Round rod	★¢10	★¢12	¢16	★¢28	★¢32	★¢40
16mm (thickness)	★16*100	★16*125		Round rod	★¢45	★¢46	★¢50	★¢55	★¢60	★¢65
20mm (thickness)	★20*80	★20*100			★¢70	★¢75	★¢80

 

Round angle aluminium busbar
2mm (thickness)	R2*20
3mm (thickness)	R3*30	R3*40	R3*50	R3*60	R3*80	R3*100	R3*120	R3*160
4mm (thickness)	R4*25	R4*30	R4*40	R4*50	R4.7*151
5mm (thickness)	R5*30	R5*35	R5*40	R5*50	R5*60	R5*120
6mm (thickness)	R6*50	R6*60	R6*80	★R6.3*63	R6*100	R6*120	R6*140	R6*160
8mm (thickness)	R8*40	R8*50	R8*60	★R8*63	R8*80	R8*100
10mm (thickness)	R10*50	R10*60	R10*80	R10*100	★R10*120	R10*125	R10*170	R10.4*25
12.5mm (thickness)	★R12.5*80	★R12.5*125		★R16*120

                         Mechanical Properties of Aluminum Bus Conductor and Related Alloys
         (The Aluminum Association ; ASTM B 236, B 241, and B 429; and Manufacturer's Listings)
 

Product	Alloy and Temper	Thickness in Ultimates	Tensile Strength (ksi) At 20 (68.F)		Typical  Ultimate	Typical Yield	Typical(a)  Elongation (Percent - in 2 in.  Or 4 Dia)
			Minimum  Ultimate	Minimum  Yield
Extruded rod, bar tube, pipe and shapes	1350-H111	All	8.5	3.5			35.0
	6101-T6	0.125-0.500	29.0	25.0	32.0	28.0	15.0
	6101-T61	0.125-0.749 0.750-1.499 1.500-2.000	20.0 18.0 15.0	15.0 11.0 8.0
	6101-T63 6101-H111 6101-T64 6101-T65	0.125-0.500 0.250-2.000 0.125-1.000 0.125-0.749	27.0 12.0 15.0 25.0	22.0 8.0 8.0 20.0	14.0	11.0
Extruded pipe(c)	6061-T6 6063-T6	Pipe size 1.0 &  over Pipe sizes,all	38.0 30.0	35.0 25.0	45.0 35.0	40.0 31.0	10.0 min 8.0 min
Rolled bar	1350-H12	0.125-1.000	12.0	8.0	14.0	12.0
Sawed-plate bar or sheet	1350-H112	0.125-0.499 0.500-1.000 1.001-3.000	11.0 10.0 9.0	6.0 4.0 3.5			10.0min 16.0min 22.0min
Rolled sheet (for shearing or forming)	1350 1350-H12 1350-H14	0.020-0.249	8.0 12.0 14.0		12.0 14.0 16.0	4.0 12.0 14.0	20-30 min 4-9 min 3-6 min
	1350-H16 1350-H18	0.020-0.125	16.0 18.0		18.0	16.0	2-4 min 2-4 min