5A06 O H12 Aircraft Aerospace Aviation Aluminum Alloy Plate Sheet

• Application: Transportation Tools, Aviation
• Certification: RoHS, ISO9001, JIS, GB, EN
• Technique: Hot Rolled
• Grade: 5000 Series
• Temper: O/H12
• Surface Treatment: Mill Finish
• Model NO.: 5A06
• Alloy: Alloy
• Transport Package: Export Standard Wooden Pallet
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7606125900
• Production Capacity: 15000mt/Month

Product Description

5A06 aluminum alloy sheet round bar tube wire

The content of Mg in 5A06 alloy is the highest, 6.3%, and the content of Mn is 0.65%, and the average total content of Mg and Mn is 7%. Because of its high strength, low plasticity, good corrosion resistance and weldability, can be processed into a plate, tube, rod, profiles, wire and forging die forging, etc., 5A06 aluminum alloy sheet round bar tube wire are widely used in aviation, aerospace, ships, automobiles, ships, missiles, tanks and other industries.
 

Chemical composition of 5A06 alloy
Alloy	Si	Fe	Cu	Mn	Mg	Zn		Ti	Others		Al
									Each	Others
5A06	0.4	0.4	0.4	0.50~0.8	5.8~6.8	0.2	0.0001~0.005	0.02~0.10	0.05	0.15	Remainder

 

Calibration mechanical strength of 5A06 aluminum alloy sheet round bar tube wire
Technical standard	Type	Temper	δ  or d/mm	Tension strength Rm/Mpa	Rp0.2/Mpa	A/%
YS/T 213 YS/T 215	Aluminum sheet	O	0.5~4.5	314	157	15
GB/T 3880	Aluminum sheet	O	0.5~4.5	315	155	16
		H112	5.0~10.0	315	155	16
GB/T 3880	Aluminum sheet	H112	>10.0	305	145	12
			>12.5	305	145	12
			>25.0	295	135	6
GJB 2662	Aluminum plate	H112	7~10	315	157	15
			>10~25	305	147	11
			>25~50	295	137	6
GB/T 3191	Extruded aluminum round bar	H112, O	≤200	315	157	15
			>200	284	118	10
GJB 2504	Extruded aluminum round bar		5~150	315	157	15
			>150	280	120	10
HB 5202	Extruded aluminum round bar		≤240	314	157	15
GJB 2507	Extruded aluminum round bar	H112, O	All	314	157	15
GB/T 4437	Aluminum tube	H112	All	314	147	15
GJB 2381	Aluminum tube	H112	>25~150	315	147	12
			>180	315	147	10
		H112	>25~180	315	147	15
			>180	315	147	12
GJB 2379	Cold drawn aluminum tube	O	All	≤215	≥88	≥15
GJB 2351	Free forgings,Die forgings	H112	As agreed	≥196 ≥220	- -	≥10 ≥12
GJB 2055, GB/T 3196	Aluminum wire	H×8	1.6~10.0	167	-	-

 

Technical Standard	Alloy	Weight/KG	L			LT			ST		HB
			Rm/Mpa	Rp0.2/Mpa	A5/%	Rm/Mpa	Rp0.2/Mpa	A5/%	Rm/Mpa	A5/%
GJB 2351-1995	H112 O	>60	284	118	11.0	284	118	11.0	284	11.0	-
		>30	294	127	14.0	294	127	14.0	294	14.0	-
		≤30	304	127	14.0	304	127	14.0	304	14.0	-
HB 5204	O	≤60	304	127	14.0	304	127	14.0	304	14.0	70
		>60	284	118	11.0	284	118	11.0	284	11.0	70