Aluminum Alloy Extruded Seamless Tubes (6005/6005A/6041/6042/6061)

• Customization: Available
• Type: Decoration Aluminium Profile, Transport Aluminium Profile, Industrial Aluminium Profile
• Shape: Square/Round/Flat/or as Customers′ Drawing
• Model NO.: 6005/6005A/6041/6042/6061
• Grade: 6000 Series
• Temper: T1/T5/T6511
• Alloy: Alloy
• Surface Finishing: Mill Finish/Polished/Anodizing/Brushing
• Alloying Ingredient: 6005/6105/6041/6042
• Certification: CE, ISO, ISO9001:2008/SGS
• Polished Aluminum Profile: Mechanical Polishing
• Normal Anodizing Thickness: 8-15 Micro
• Color: Any
• Deep Process: CNC, Drilling, Milling, Cutting, Welding
• Service: OEM and ODM
• Transport Package: Ep Paper Inside, Craft Paper/Pallet Outside.
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7604210000
• Production Capacity: 10000mt/Month

Product Description

Aluminum Alloy Extruded Seamless Tubes(6005/6005A/6041/6042/6061)

6005 alloy is widely used for extrusion of general aluminum material. All extruded sections and pipes that require material strength more than 6063 alloy can be produced by this alloy. Like 6063 alloy, they are pure Al-Mg-Si alloy. Except Mg and Si, no alloying elements are contained, Mg2Si is the only strengthening phase, and all Mg and Si form Mg2Si. It has excellent extrusion performance and low quench sensitivity, and can be used for on-line quenching of the extruder. The material with wall thickness less than 3mm can be air-cooled quenching. Another prominent advantage of them is the smooth surface and easy anodizing and coloring. 6005 alloys are currently widely used for extruding sections and pipes of products such as ladders, wheelchairs, television antennas, and platform frames. However, it should be noted that 6005 alloys are not made to bear the impact load structure.

6005 alloy is widely used for extrusion of general aluminum material. All extruded sections and pipes that require material strength more than 6063 alloy can be produced by this alloy. Like 6063 alloy, they are pure Al-Mg-Si alloy. Except Mg and Si, no alloying elements are contained, Mg2Si is the only strengthening phase, and all Mg and Si form Mg2Si. It has excellent extrusion performance and low quench sensitivity, and can be used for on-line quenching of the extruder. The material with wall thickness less than 3mm can be air-cooled quenching. Another prominent advantage of them is the smooth surface and easy anodizing and coloring. 6005 aluminum tube pipe are currently widely used for extruding sections and pipes of products such as ladders, wheelchairs, television antennas, and platform frames. However, it should be noted that 6005 alloys are not made to bear the impact load structure.

Specification:
Alloy: 6005 6105 6041 6042
Temper: T1,T5,T6511
OD: 3--130mm
ID: 3--100mm
Length: 1000mm--6000mm
 

Chemical Composition
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ga	V	Ti	Other	Min.Al
6005	0.6-0.9	0.35	0.10	0.10	0.40-0.60	0.10	-	0.10	-	-	0.10	0.15	Remainder
6105	0.6-1.0	0.35	0.10	0.10	0.45-0.8	0.1	-	0.1	-	-	0.1	0.15	Remainder
6041	0.5-0.9	0.15-0.70	0.15-0.60	0.05-0.20	0.8-1.2	0.05-0.15	-	0.25	-	-	0.15	0.15	Remainder
6042	0.5-1.2	0.70	0.2-0.6	0.40	0.7-1.2	0.04-0.35	-	0.25	-	-	0.15	0.15	Remainder

  

Physical Property
Alloy	Temper	Wall thickness /mm	Room temperature Test Result
			Tension Strength/MPa	Yield Strength/MPa	Elongation/%
					A50mm	A
			Not less than
6005	T1	≤12.50	170	105	16	14
	T5	≤3.20	260	240	8	-
		3.20~25.00	260	240	10	9
6105	T1	≤12.50	170	105	16	14
	T5	≤12.50	260	240	8	7
6041	T5,T6511	10.00~50.00	310	275	10	9
6042	T5,T6511	10.00~12.50	260	240	10	-
		12.50~50.00	290	240	-	9