2A50 Aluminum Forgings Forged Product Parts

• Customization: Available
• Processing Object: Metal
• Molding Style: Hot Forging
• Model NO.: 2A50
• Molding Technics: Gravity Casting
• Application: Aviation
• Material: Aluminium
• Heat Treatment: Quenching
• Surface Treatment: Zinc/Chrome Plating,Anodizing
• Forging Tolerance: +/-0.2mm
• Standard: ANSI
• Certification: CE, ISO 9001:2008
• Service: OEM ODM
• Transport Package: Export Standard Wooden Pallet or as Your Requsts
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7218100000
• Production Capacity: 5000pieces/Month

Product Description

2A50 is a high strength forged Al-Cu-Mg-Si alloy, which can be strengthened by heat treatment. In hot state, it has high plasticity and is easy to forge and stamp. After solution treatment and artificial aging, it has high strength and good process plasticity, but it has extrusion effect, and its longitudinal and transverse properties are different. The corrosion resistance of the alloy is good, but there is a tendency of intergranular corrosion. The resistance spot welding and seam welding have good weldability, while the arc welding and gas welding have poor performance. Its cutting performance is good.

Because of its good casting properties, 2A50 aluminum alloy is suitable for producing large cross-section ingots. It is used as the blank of large hot-forged parts, such as partition frame, bracket and rocker arm of aircraft. It is also used to manufacture medium and small forgings and die forgings with complex shape and medium strength.
 

Mechanical Properties of 2A50 Die Forgings and Free Forgings as stipulated in Technical Standards
	Temper	Direction	Tensile strength Rm/MPa	Prescribed plastic elongation strength Rp0.2/MPa	Elongation A (%)
Free forgings	T6	Portrait	365	-	9.0
	T6	Long transverse	345	-	6.0
Die forgings	T6	Portrait	380	275	11.0
	T6	Long transverse	365	245	7.0

 

Tensile Properties of 2A50 Aluminum Alloy Forgings Stabilized at Room Temperature
Temper	Stabilization treatment		Tension strength Rm/MPa	Elongation A (%)
	Temperature/ºC	Holding time /h
T6	20	-	392	12
	200	0.5	275	15
		100	221	18
T6	250	0.5	177	16
		100	98	35
	300	0.5	103	23
		100	64	45

The time interval between solution quenching and aging strengthening of 2A50 aluminium alloy should be less than 6 h, the overburning temperature should be 545 ºC, and the forging temperature should be 470-370 ºC.
 

Type	Alloy	Projected area(m2)Or weight(kg)	Temper	Standard
Free forgings	5 series	≤3000kg	O,F	GBn223     ASTMB247
	2,6,7 series	≤3000kg	T6,T4,O,F
Mould forgings	5 series	≤2.5m2	O,F
	2,6,7 series	≤2.5m2	T6,T4,O,F