6082 Aluminum Alloy Busbar

• Customization: Available
• Shape: Flat
• Application: Transportation Tools, Door & Window, Glass Wall, Heat Sink, Decorations
• Model NO.: 6082
• Certification: ISO9001, ASTM, JIS, GB, EN
• Technique: Extruded
• Grade: 6000 Series
• Temper: T3 - T8
• Surface Treatment: Mill Finish
• Alloy: Non-alloy
• Thickness: up to 200mm
• Width: up to 600mm
• Length: up to 6000mm
• Tensile: 45,000 +/-
• Transport Package: Export Standard Wooden Pallet, Box
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7606119000
• Production Capacity: 15000mt/Month

Product Description

6082 Aluminum Alloy Busbar
Aluminium alloy 6082 is a medium strength alloy with excellent corrosion resistance. It has the highest strength of the 6000 series alloys. Alloy 6082 is known as a structural alloy. In plate form, 6082 is the alloy most commonly used for machining. As a relatively new alloy, the higher strength of 6082 has seen it replace 6061 in many applications. The addition of a large amount of manganese controls the grain structure which in turn results in a stronger alloy. It is difficult to produce thin walled, complicated extrusion shapes in alloy 6082. The extruded surface finish is not as smooth as other similar strength alloys in the 6000 series.
In the T6 and T651 temper, alloy 6082 machines well and produces tight coils of swarf when chip breakers are used.
Place of Origin : Henan China(Mainland)
Application of Aluminum Bars :
Aluminum bars can be used in aircraft structures, rivet, missile components, truck wheel hub, screw propeller and other structural components.
 
Technical Parameters :
Alloy:6060 , 6061, 6063, 6082,  
Standard :
GB/T3191,ASTM B221,211,BS1474,ISO209, EN573,JISH4000
Grade :
1,2,3,5,6,7 series.
Temper : H112, T4, T6, T651,T6510

Chemical Properties

Alloy	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ti	Ga	V	Others		Aluminium min.
												Each	Total
6082	0.7-1.3	0.5	0.1	0.4-1.0	0.6-1.2	0.25	-	0.2	0.1	-	-	0.05	0.15	Remainder

Mechanical properties according to EN755-2

Temper*	Thickness  e**	Yield stress Rp0.2 (mpa)	Tensile strength Rm (mpa)	Elongation A[%]	Elongation A50mm [%]	Hardness ** HB
T4	e<=25	110	205	14	12	65
T5	e<=5	230	270	8	6	80
T6	E<=5	250	290	8	6	95
	5<e<=25	260	310	10	8	95

Physical properties (approximate values, 20ºC)

Density [kg/m3]	Melting range [ºC]	Electrical Conductivity [MS/m]	Thermal  Conductivity [W/m.K]	Co-efficient of Thermal expansion 10-6/k	Modulus of elasticity [GPa]
2700	585-650	24-32	170-220	23.4	≈70

Properties
Aluminium and Copper Specifications

Parameters	Aluminium	Copper
Relevant Standards	IEC 60105 ISO 209-1,2	IEC 60028
Physical Properties Chemical Composition Specific Heat     gm.cal/ºC Density         gm/cm2 Melting Point    ºC	0.092 2.91 660	99% pure 0.220 8.89 1083
Mechanical Properties Ultimate Tensile Strength      kgf/mm2 Ultimate Shearing Strength    kgf/mm2 Elastic Modulus             kgf/mm2 0.2% Tensile-proof Strength   kgf/mm2	20.5/25 15 6,700 16.5/22	22-26 16-19 12000 60-80% of tensile strength
Electrical Properties Specific Resistance         cm Volume Conductivity       mm2 Conductivity              % IACS Co-efficient of expansion    mm/m/ºC	3.133 31.9 57 2.3*10-5	1.7241 58 100 1.73*10-5