2A16 aluminum coil strip
2A16 aluminum coil strip is used for axial compressor blades of turbojet engines with working temperature of 200~300ºC and other die forgings that work at high temperature and whose alloy performance can meet the structural requirements. It is generally used as the main load-bearing structural material.
2A16 aluminum coil strip is a kind of heat-resistant duralumin, which is characterized by not too high strength at room temperature, but higher creep strength at high temperature. The alloy has higher plasticity in hot state without extrusion. The effect can be strengthened by heat treatment, and the welding performance of spot welding, seam welding and argon arc welding is good, the tendency to form cracks is not significant, and the air tightness of the weld is good. The corrosion stability of the weld is low, the corrosion stability of the aluminum-clad sheet is good, and the corrosion resistance of the extruded semi-finished product is not high. In order to prevent corrosion, anodizing treatment or painting should be used to protect the cutting performance.
Advantages of 2A16 aluminum coil strip:
1. Good corrosion stability
2. Good weldability.
3. Good machinability.
Alloy: 2A16
Temper: O, T4, T6, T62
Thickness: 0.3-4.0mm
Width: 1000-2600mm
| Alloy |
Si |
Fe |
Cu |
Mn |
Mg |
Zn |
Zr |
Ti |
Cr |
| 2A16 |
0.30 |
0.30 |
6.0-7.0 |
0.4-0.8 |
0.05 |
0.10 |
0.20 |
0.10-0.20 |
-- |
Mechanical property:
| Alloy |
Temper |
Thickness (mm) |
Tensile Strength (MPa) |
Yield Strength (MPa) |
Elongation A50% |
Standard |
| 2A16 |
O |
1.0--4.0 |
≤235 |
-- |
15 |
GB/T 3880 EN485 ASTM B209 |
| T4 |
275 |
-- |
12 |
| T6 |
375 |
275 |
8 |
| T62 |
375 |
265 |
8 |
2A16 aluminum coil strip is used for working parts below 250~350ºC, such as axial II exhauster blades, discs, and plates are used as welding parts that work at room temperature and high temperature, such as containers, airtight cabins, etc.