2014 Aluminum Forgings Forged Product Parts

• Customization: Available
• Processing Object: Metal
• Molding Style: Hot Forging
• Model NO.: 2014
• Molding Technics: Gravity Casting
• Application: Aviation
• Material: Aluminium
• Heat Treatment: Quenching
• Surface Treatment: Zinc/Chrome Plating,Anodizing
• Forging Tolerance: +/-0.2mm
• Standard: ANSI
• Certification: CE, ISO 9001:2008
• Service: OEM ODM
• Transport Package: Export Standard Wooden Pallet or as Your Requsts
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7218100000
• Production Capacity: 5000pieces/Month

Product Description

2014 is a high strength forged Al-Cu-Mg-Si alloy, which can be strengthened by heat treatment. The chemical composition of the alloy is similar to that of 2114 aluminium alloy. It has high strength, good hot working property and is easy to forge. The performances are basically the same as 2114. Because of the high copper content, the alloy has poor corrosion resistance, intergranular corrosion and stress corrosion tendency. It has good weldability and cutting performance.


2014 is used to manufacture wheel rings with high strength, high hardness and high load, such as wheel rings, truck frame and suspension assembly, fuel tank and structural parts of rocket booster, etc. It can also produce 2014 coated aluminium material to improve its corrosion resistance.
 

High Temperature Tensile Properties of 2014 Aluminum Alloy at Different Temperatures
Temper	Temperature/ºC	Tension strength Rm/MPa	Prescribed plastic elongation strength Rp0.2/MPa	Elongation A (%)
T6	100	439	393	15
	150	276	241	20
	204	110	90	38
T6	260	66	52	52
	315	45	34	65
	370	30	24	72

In heat treatment of 2014 aluminium alloy, the suitable temperature of coolant for thin-walled parts with complex structure (wall thickness less than 30 cm) is 60-80 ºC. This process parameter can avoid deformation or warping of parts during quenching.
The alloy has good plasticity in hot state and can be used to manufacture short sword and die forgings with complex shapes. The formability is poor in cold condition, and the forging temperature usually ranges from 440 to 320 ºC

Type	Alloy	Projected area(m2)Or weight(kg)	Temper	Standard
Free forgings	5 series	≤3000kg	O,F	GBn223     ASTMB247
	2,6,7 series	≤3000kg	T6,T4,O,F
Mould forgings	5 series	≤2.5m2	O,F
	2,6,7 series	≤2.5m2	T6,T4,O,F