6101 Aluminium Coil Strip

• Customization: Available
• Application: Transportation Tools, Decorations, Lighting, Printing
• Certification: ISO9001, ASTM, GB, EN
• Model NO.: 6101
• Technique: Hot Rolled/Cast Rolled
• Grade: 6000 Series
• Temper: F\O\H112\H12\H14\H24\H18\H16\H26\H32\H34
• Surface Treatment: Mill Finish
• Alloy: Alloy
• Thickness: 0.8-6mm
• Width: 800-1700mm
• Transport Package: Export Standard Wooden Pallet
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7606119000
• Production Capacity: 10000mt/Month

Product Description

6101 Aluminium Coil Strip
6101 Anodised Aluminium Strip / Stripping Aluminum in China

The materials of the aluminum strip are cast rolled aluminum coil and hot rolled aluminum coil that are rolled into thin aluminum coil of different thickness and width by cold rolling Mills, and then cut vertically into aluminum strip of different width by longitudinal shear machines according to usage.

Aluminium / Aluminum alloys have good corrosion resistance. The strength of these alloys can be reduced when they are exposed to high temperatures. However, their strength can be increased at subzero temperatures. Aluminium / Aluminum 6101 alloy has good mechanical strength and high electrical conductivity.

Chemical Properties - 6101 Aluminium Coil Strip

Alloy Designation

Si

Fe

Cu

Mn

Mg

Cr

Ni

Zn

Ti

Ga

V

Remarks

Others

Aluminium min

Numerical

Chemical Sympols

Each

Total

EN AW -6101

EN AW- AI MgSi

0.3-0.7

0.5

0.1

0.03

0.35-0.8

0.03

-

0.10

-

-

-

0.06

0.03

0.10

Remainder

Physical Properties - 6101 Aluminium Coil Strip
The physical properties of  Aluminium / Aluminum 6101 alloy are given in the following table.

Properties	Metric	Imperial
Density	2.7 g/cm3	0.0975 lb/in3
Melting point	588°C	1090°F

Mechanical Properties - 6101 Aluminium Coil Strip
The mechanical properties of Aluminium / Aluminum 6101 alloy are tabulated below.

Properties	Metric	Imperial
Tensile strength	97 MPa	14069 psi
Yield strength	76 MPa	11023 psi
Elastic modulus	70-80 GPa	10153-11603 ksi
Poisson's ratio	0.33	0.33

Thermal Properties - 6101 Aluminium Coil Strip
The thermal properties of Aluminium / Aluminum 6101 alloy are given in the following table.

Properties		Conditions
		T (ºC)	Treatment
Thermal expansion	23 (10-6/ºC)	20-100	-
Thermal conductivity	218 W/mK	25	T6

Fabrication and Heat Treatment
Machinability
Aluminium / Aluminum 6101 alloy has good machinability. Oil base lubricant is used to perform machining operations. Carbide or high speed tool steel tooling can be used for machining this alloy.
 
Forming
Aluminium / Aluminum 6101 alloy can be formed using conventional methods.
 
Welding
Aluminium / Aluminum 6101 alloy can be welded using all standard welding methods. Inert gas arc welding method is the most preferred method for welding this alloy. The strength of the subsequent parts will be reduced when welded in the heat treated condition.
 
Heat Treatment
Aluminium / Aluminum 6101 alloy does not react to heat treatment. However, heat treatment can be done by annealing and aging.
 
Cold Working
Aluminium / Aluminum 6101 alloy can be cold worked in the aged or annealed conditions.
 
Annealing
Aluminium / Aluminum 6101 alloy is annealed at 413°C (775°F) for 3 h followed by controlled cooling at 10 to 260°C (50 to 500°F) per hour, and cooling in air. Stress relief annealing process can also be performed after cold working at 344°C (650°F) followed by cooling in air.
 
Aging
Aluminium / Aluminum 6101 alloy can be aged at different temperatures and times based on the finished temper. For example, T6 can be aged at 177°C (350°F) for 20 h, T61 can be aged at 227°C (440°F) for 6 h, and T63 can be aged at 194°C (380°F) for 19 h followed by cooling in air.
 
Hardening
Aluminium / Aluminum 6101 alloy can be hardened by cold working and aging.
 
Applications
Aluminium / Aluminum 6101 alloy is used in electrical bus bar conductor applications for enclosed bus electrical installations.