6151 Aluminum Forgings Forged Product Parts

• Customization: Available
• Processing Object: Metal
• Molding Style: Hot Forging
• Model NO.: 6151
• Molding Technics: Gravity Casting
• Application: Aviation
• Material: Aluminium
• Heat Treatment: Quenching
• Surface Treatment: Zinc/Chrome Plating, Anodizing
• Forging Tolerance: +/-0.2mm
• Standard: ANSI
• Certification: CE, ISO 9001:2008
• Service: OEM ODM
• Transport Package: Export Standard Wooden Pallet or as Your Requsts
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7218100000
• Production Capacity: 5000pieces/Month

Product Description

6151 alloy T6 T652 aluminum forgings are generally used for forging crankshaft parts. Machine parts and rolling ring conducting mine and machine parts have good forgability, high strength and corrosion resistance. All parts requiring good forging performance, high strength and good corrosion resistance can be processed with this alloy.

Process characteristics

The annealing standard of 6151 alloy is 413ºC/(2h~3h). The cooling rate of 6151 alloy is not more than 27ºC/h. The alloy is cooled to 260 ºC with the furnace, and then air-cooled out of the furnace. Solid solution treatment temperature (510ºC~525ºC)/4min, quenching in room temperature water, quenching in 65ºC~100ºC water for large forgings. Artificial aging code(165ºC~175ºC)/(8h~12h). The hot working temperature ranges from 260 ºC to 480 ºC.

Mechanical property
The minimum mechanical properties of 6151 alloy are 50mm or 4D (d is sample diameter). 6151 alloy has no low temperature brittleness and can be used to process parts working at extremely low temperature. At 25 ºC, the tensile strength Rm = 330N/mm2, yield strength Rp0.2 = 298N/mm2, elongation A = 17%, and temperature drops to 200 ºC, the properties of 6151 alloy increase completely, reaching 395N/mm2, 345N/mm2 and 20%, respectively. The working temperature of 6151 alloy should not exceed 120 ºC.
 

Alloy	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ti	Ga	Others		Alu
											Each	Toal
6151	0.6--1.2	1.0	0.35	0.20	0.45--0.8	0.15--0.35	--	0.25	0.15	--	0.05	0.15	Remainder

 

Tensile mechanical properties of 6151 aluminium alloy forgings
Temper		Tension strength Rm/MPa	Prescribed plastic elongation strength Rp0.2/MPa	Elongation A (%)
Mould forgings T6	Axis parallel to grain flow direction	303	225	14
	Axis parallel to grain flow direction	303	255	6
Forged ring T6,T652	Radial direction	303	255	5
	Axial direction	303	241	4
	Radial direction	290	241	2

 

Type	Alloy	Projected area(m2)Or weight(kg)	Temper	Standard
Free forgings	5 series	≤3000kg	O,F	GBn223     ASTMB247
	2,6,7 series	≤3000kg	T6,T4,O,F
Mould forgings	5 series	≤2.5m2	O,F
	2,6,7 series	≤2.5m2	T6,T4,O,F