Aircraft Aerospace Extruded Aluminum Round Bar for Aviation

• Customization: Available
• Type: Transport Aluminium Profile, Industrial Aluminium Profile, Aviation
• Shape: Round/Flat/Angle/Square/ Hexagon
• Model NO.: 2024/3A21/5A03/6A02/7A04/7149
• Grade: 2000 Series/3000 Series/5000 Series/6000 Series
• Temper: O/H112/T3/T6/T73/T74/T8511
• Alloy: Alloy
• Surface Finishing: Anodized,Electrophoresis,Powder/PVDF Coated.
• Alloying Ingredient: 2024/3A21/5A03/6A02/7A04/7149
• Certification: ISO, En755 GB5237-2008 Astmb221 DIN
• Extrusion Machine: 1000-4000 Tons, 35 Press Lines.
• Transport Package: Export Standard Wooden Pallet or as Your Requsts
• Specification: According to Customer Requirement
• Trademark: Chalco Aluminum
• Origin: Henan China
• HS Code: 7604210000
• Production Capacity: 4000mt/Month

Product Description

Aircraft Aerospace Extruded Aluminum Round Bar for Aviation 

Get more application of 3××× series alloys in aerospace manufacturing is 3A21, which belongs to the heat treatment can not be strengthened Aluminum Alloy, its strength is not high, but higher than 1××× series alloy, cold deformation can increases the strength and plasticity in the annealed state can be very high. Processing various semi-finished products, plate, belt, foil, tube, rod, wire type, etc., and forging and die forging. 3A21 aluminum alloy sheet profile forgings has good weldability, special welding performance excellent friction stir welding, welding, easy to hydrogen atoms and contact welding; has high corrosion resistance, equivalent to 1××× alloy machinability is poor.

3A21 aluminum alloy sheet profile forgings are mostly used in the manufacture of aircraft oil tanks, gasoline and lubricating oil ducts, cold stamping parts, rivets and small force parts.

The cold stamping performance of 3A21 alloy in annealed state is good, the state of H*4 is second, and the state of H*8 is not good. The hot state process has good plasticity. The temperature of hot die forging is 420~475 ºC.

The surface treatment performance of 3A21 alloy is good, the machinability and grinding performance are not good, but not the O state material.
 

Chemical Composition of 3A21 Alloy

Alloy

Si

Fe

Cu

Mn

Mg

Cr

Ni

Zn

Ti

Zr

Others

Al

Each

Total

3A21

0.6

0.70

0.05~0.5

1.0~1.6

0.05

0.10

~

0.10

~

~

0.05

0.15

Remainder

 

Calibrated Mechanical Strength of 3A21 Aluminum Alloy Sheet Profile Forgings
Technical Standard	Type	Test Temper	δor d/mm	Tension Strength Rm	A/%
				Not less than
YS/T 213 YS/T 215	Aluminum sheet	O	0.3~3.0	98~147	22
			>3.0	98~147	20
		H×4	0.3~6.5	147~216	6
		H×8	0.3~0.5	186	1
			>0.5	186	2
			>0.8	186	3
			>1.2	186	4
GB/T 3880	Aluminum sheet	O	>0.2	100~150	19
			>0.8		23
			>4.5		21
		H14 H24	>0.2	145~215	6
			>0.8		6
			>1.3		6
		H18	>0.2	185	1
			>0.5		2
			>0.8		3
			>1.3		4
		H112	>4.5	110	16
			>10.0	120	16
			>12.5	120	16
			>25.0	110	16
GJB 2053	Aluminum sheet	O	0.5~0.7	98~147	18
			>0.7		22
			>3.0		20
		H×4	0.5~4.0	147~215	6
		H×8	0.5~0.8	186	2
			>0.8		3
			>1.2		4
GJB 2662	Aluminum plate	O	>4	98~147	20
		H112	7~10	108	15
			>10	118	15
			>25	108	12
GB/T 3191	Extruded aluminum bar	H112, O	≤150	≤165	20
GJB 2504	Extruded aluminum bar		5~150	≤167	20
			>150	≤167	15
HB 5202	Extruded aluminum bar		≤240	≤167	20
GJB 2507	Extruded aluminum bar	H112, O	All	≤167	16
GB/T 4437	Aluminum tube	H112	All	≤167	-
GJB 2381		H112, O	25~250
GJB 2351	Cold drawn aluminum tube	O	All	≤137	-
		H×8	All	137	-
GJB 2351	Free forgings,Die forgings	H112	As agreed	≤167	20
GB/T 3196
GB/T 3196	Aluminum wire	H×8	1.6~10.0	69	-
GJB 2055